KINGFA ULTRON-C090E
- Flame retardant POM with UL 94 HB rating
- High strength with 60 MPa tensile strength
- Excellent fatigue resistance for durable components
- Good thermal resistance with HDT of 155°C
- Ideal for automotive, electrical, and industrial applications
Product Overview
KINGFA ULTRON-C090E is a flame-retardant Acetal (POM) copolymer designed for injection molding applications.
This medium-viscosity engineering thermoplastic is designed to meet the demands of automotive, electrical, and industrial components that require high strength, fatigue resistance, and good thermal stability.
It offers high tensile strength, excellent fatigue resistance, and flame retardancy, making it suitable for a wide range of applications including automotive parts, electrical components, and mechanical parts.
Key Properties
Flame Retardant: Meets UL94 HB for improved safety in electrical and automotive applications
High Strength & Fatigue Resistance: Provides 60 MPa tensile strength and excellent durability
Good Thermal Resistance: Heat Deflection Temperature (HDT) of 155°C at 0.45 MPa
Excellent Electrical Insulation: High volume resistivity and electric strength for electrical applications
Medium Viscosity: Balanced melt flow ideal for complex injection molding
Typical Applications
Automotive Components: Electrical connectors, mechanical parts, and functional automotive components
Electrical/Electronic Parts: Connectors, switches, and other electronic enclosures
Industrial Gears and Mechanical Parts: Bearings, gears, and structural components for machinery
Engineering Components: Parts requiring high strength and thermal resistance for critical applications
Technical Data (Typical Values)
Physical Properties
| Property | Value | Test Standard |
|---|---|---|
| Density | 1.41 g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.8–2.2 % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 % | ISO 62 |
Mechanical Properties
| Property | Value | Test Standard |
|---|---|---|
| Tensile Strength | 60.0 MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 32 % | ISO 527-2/50 |
| Flexural Modulus | 2500 MPa | ISO 178 |
| Flexural Stress | 78.0 MPa | ISO 178 |
| Notched Izod Impact Strength | 7.0 kJ/m² | ISO 180 |
| Rockwell Hardness (R-Scale) | 118 | ISO 2039-2 |
Thermal Properties
| Property | Value | Test Standard |
|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 155 °C | ISO 75-2/B |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 °C | ISO 75-2/A |
Electrical Properties
| Property | Value | Test Standard |
|---|---|---|
| Volume Resistivity | 1.0E+16 ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm, in Oil) | 21 kV/mm | IEC 60243-1 |
Flame Properties
| Property | Value | Test Standard |
|---|---|---|
| Flame Rating | HB | UL 94 |
Processing Parameters
| Property | Value | Test Standard |
|---|---|---|
| Drying Temperature | 80–100 °C | — |
| Drying Time | 4.0–6.0 hr | — |
| Processing (Melt) Temperature | 180–210 °C | — |
| Mold Temperature | 50–90 °C | — |
Why Choose KINGFA ULTRON-C090E
Flame Retardant: Meets UL 94 HB for enhanced safety in automotive and electrical applications
High Strength & Fatigue Resistance: 60 MPa tensile strength and excellent durability under stress
Good Thermal Resistance: 155°C HDT at 0.45 MPa for high-performance parts
Excellent Electrical Insulation: High dielectric strength and volume resistivity for safe electrical components
Medium Viscosity: Well-suited for high-throughput injection molding