KINGFA ULTRON-C090
- Flame retardant POM with UL 94 HB rating
- High strength with 62 MPa tensile strength
- Creep and fatigue resistant for long-term performance
- Good electrical insulation with high dielectric strength
- Suitable for automotive, electrical, and industrial applications
Product Overview
KINGFA ULTRON-C090 is a flame-retardant Acetal (POM) homopolymer designed for high-performance injection molding applications.
This medium-viscosity engineering thermoplastic provides excellent creep resistance, high strength, and fatigue resistance, making it suitable for demanding applications in automotive, electrical, electronic, and industrial components.
It offers high mechanical performance under load and maintains good electrical insulation properties, ensuring reliable performance in high-stress environments.
Key Properties
Flame Retardancy: Meets UL 94 HB for enhanced safety in electrical and automotive applications
High Strength: 62 MPa tensile strength and 80 MPa flexural strength for durable components
Creep & Fatigue Resistance: Excellent performance under long-term loads
Good Electrical Insulation: High volume resistivity and dielectric strength
Medium Viscosity: Optimized for balanced flow in injection molding applications
Typical Applications
Automotive Components: Engine parts, connectors, and functional components
Electrical/Electronic Parts: Relays, connectors, switches, and circuit boards
Industrial Gears and Mechanical Parts: Bearings, gears, and mechanical components
Engineering Components: Structural parts requiring high strength and resistance
Technical Data (Typical Values)
Physical Properties
| Property | Value | Test Standard |
|---|---|---|
| Density | 1.41 g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.8–2.2 % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 % | ISO 62 |
Mechanical Properties
| Property | Value | Test Standard |
|---|---|---|
| Tensile Strength | 62.0 MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 35 % | ISO 527-2/50 |
| Flexural Strength | 80.0 MPa | ISO 178 |
| Flexural Modulus | 2500 MPa | ISO 178 |
| Notched Izod Impact Strength | 7.0 kJ/m² | ISO 180 |
| Rockwell Hardness (R-Scale) | 118 | ISO 2039-2 |
Electrical Properties
| Property | Value | Test Standard |
|---|---|---|
| Volume Resistivity | 1.0E+16 ohms-cm | IEC 60093 |
| Electric Strength (2.00 mm, in Oil) | 21 kV/mm | IEC 60243-1 |
Flame Properties
| Property | Value | Test Standard |
|---|---|---|
| Flame Rating | HB | UL 94 |
Processing Guidelines
| Property | Value |
|---|---|
| Drying Temperature | 80–100 °C |
| Drying Time | 4.0–6.0 hr |
| Processing (Melt) Temperature | 180–210 °C |
| Mold Temperature | 50–90 °C |
Why Choose KINGFA ULTRON-C090
Flame Retardant: Meets UL 94 HB for enhanced safety in electrical and automotive applications
High Strength: Provides durability with 62 MPa tensile strength and 80 MPa flexural strength
Creep & Fatigue Resistant: Maintains long-term performance under load
Good Electrical Insulation: High dielectric strength and volume resistivity
Medium Viscosity: Ideal for balanced flow in injection molding processes