HIGHSUN MEIDA PA6 M2400
- Flame retardant UL94 V-2 polyamide
- Ideal for compounding and modification
- High strength and flexibility
- Excellent impact resistance
- Suitable for textile and industrial applications
Product Overview
Highsun Meida PA6 M2400 is a Polyamide 6 base polymer engineered for use in compounding and microfiber applications.
This grade offers a balanced mechanical property profile with good strength, flexibility, and impact resistance, making it ideal for further modification and high-value textile applications. It also meets UL94 V-2 flame retardancy requirements for added safety in electronics and consumer applications.
Key Properties
Base Polymer for Compounding: Ideal for creating specialized compounds and masterbatches
Flame Retardant: Meets UL94 V-2 for consumer and electronic components
Good Processability: Suitable for high-value textile and industrial applications
Versatile Mechanical Properties: Offers high strength, flexibility, and impact resistance
Good Thermal Stability: Suitable for a variety of processing conditions
Typical Applications
Masterbatch & Compound Base Resin: For further material modification
Microfiber and Textile Filaments: Ideal for textile applications
Injection Molded Industrial Parts: Suitable for durable, high-performance parts
Flame-retardant Consumer & Electronic Components: Compliant with UL94 V-2 standards
Technical Data (Typical Values)
| Property | Value / Range | Test Standard |
|---|---|---|
| Relative Viscosity (96% H₂SO₄) | 2.46 ± 0.07 | FZ/T 51004 |
| Moisture Content | ≤ 0.06 % | FZ/T 51004 |
| Hot Water Extractables | ≤ 0.7 % | FZ/T 51004 |
| Density | 1.14 g/cm³ | — |
| Tensile Strength | 60–70 MPa | — |
| Tensile Elongation at Break | 20–80 % | ASTM D638 |
| Tensile Modulus at Yield | 1900–2300 MPa | — |
| Flexural Strength | 95–105 MPa | ASTM D790 |
| Flexural Modulus | 1800–2200 MPa | — |
| Notched Impact Strength | 50–60 J/m | ASTM D256 |
| Hardness (Shore D) | 70–80 HD | ASTM D2240 |
| Molding Shrinkage | 1.0–2.0 % | ASTM D955 |
| Melt Flow Rate (MFR) | 30–38 g/10 min | ASTM D1238 |
| Heat Deflection Temperature | 65–75 °C | ASTM D648 |
| UL94 Flame Rating | V-2 | UL94 |
Why Choose Highsun Meida PA6 M2400
Versatile Base Polymer: Perfect for compounding and further modification
Flame Retardant: Complies with UL94 V-2 standard for consumer and electronic parts
Balanced Mechanical Properties: Strong, flexible, and impact-resistant
Good Processability: Suitable for both textile and industrial use
Thermal Stability: Can be processed under various conditions for demanding applications