HIGHSUN MEIDA PA6 M2000
- Modified PA6 with UL94 V-2 flame retardant
- High tensile strength and impact resistance
- Low shrinkage for precision molding
- Excellent processability
- Suitable for automotive, electrical, and toy applications
Product Overview
Highsun Meida PA6 M2000 is a modified Polyamide 6 base polymer designed for demanding applications such as automotive, electronics, electrical components, and toys. It provides a balanced set of mechanical properties, including high tensile strength, good impact resistance, and dimensional stability. With a UL94 V-2 flame retardant rating, it meets safety standards for components requiring both performance and compliance.
Key Properties
High tensile and flexural strength for durable and structural applications
UL94 V-2 flame retardant rating for enhanced safety
Good processability with moderate melt flow, suitable for injection molding
Low shrinkage contributes to dimensional stability in molded parts
Good impact resistance with decent toughness
Typical Applications
Automotive interior parts and functional components
Electrical housings and connectors
Consumer electronics and toy parts
Industrial components requiring flame retardancy
Technical Data (Typical Values)
Material Specific Properties
| Property | Value | Test Standard |
|---|---|---|
| Relative Viscosity (96% H₂SO₄) | 2.0 ± 0.07 | FZ/T 51004 |
| Moisture Content | < 0.06 % | FZ/T 51004 |
| Hot Water Extractables | < 0.7 % | FZ/T 51004 |
| Density | 1.14 | — |
Mechanical Properties
| Property | Value | Test Standard |
|---|---|---|
| Tensile Strength at Break | 72 MPa | — |
| Tensile Elongation at Break | 41 % | ISO 527 |
| Tensile Modulus | 2099 MPa | — |
| Flexural Strength | 99 MPa | ISO 178 |
| Flexural Modulus | 2514 MPa | — |
| Notched Impact Strength | 6 kJ/m² | ISO 180 |
| Hardness (Shore D) | 76 HD | ISO 868 |
| Molding Shrinkage | 0.82 / 0.93 % | — |
Thermal & Flame Properties
| Property | Value | Test Standard |
|---|---|---|
| Melt Flow Rate (MFR) | 23 g/10 min | ISO 1133 |
| Heat Deflection Temperature | 58 °C | ISO 75 |
| UL94 Flame Rating | V-2 | UL94 |
Appearance
| Property | Value |
|---|---|
| Chromaticity L* | 76.59 |
| Chromaticity a* | -2.21 |
| Chromaticity b* | -6.39 |
Why Choose Highsun Meida PA6 M2000
Flame retardant with UL94 V-2 for safety
Good processability for injection molding applications
Dimensional stability with low shrinkage
Durable with high tensile strength and impact resistance
Suitable for automotive, electrical, and toy applications