HENGYI PA6 HY245
- High melt flow PA6
- Excellent elongation for impact-resistant compounds
- Low extractables and moisture for stable processing
- Suitable for automotive, electronics, and industrial components
- High performance for fast injection molding and complex parts
Product Overview
Hengyi PA6 HY245 is a high flow Polyamide 6 (PA6) resin that offers excellent elongation, toughness, and good processability.
This grade is specifically designed for compounding and injection molding applications across a range of industries, including automotive, consumer electronics, and industrial components. Its high melt flow ensures fast cycle times, making it ideal for thin-walled and complex parts.
Key Properties
High Melt Flow: Ensures efficient processing, especially for thin-walled and complex parts
Excellent Elongation: Provides superior toughness and ductility for impact-modified compounds
Low Extractables & Moisture: Contributes to stability and consistency during processing
Balanced Stiffness & Strength: Offers good mechanical performance for a variety of applications
Versatile Base Resin: Ideal for compounding with additives, modifiers, and reinforcements
Typical Applications
Automotive: Interior and functional components, such as dashboards and trims
Consumer Electronics: Housings for appliances, phones, and other electronic devices
Toys and Furniture: Injection molded parts for durability and safety
Industrial Components: Gears, mechanical parts, and housings for industrial machinery
Technical Data (Typical Values)
Material Specific Properties
| Property | Value | Test Standard |
|---|---|---|
| Relative Viscosity (96% H₂SO₄) | 2.44 | Internal Standard |
| Hot Water Extractables | 0.25 % | Hot Water Extraction |
| Moisture Content | 491 ppm | Karl Fischer Method |
Mechanical Properties
| Property | Value | Test Standard |
|---|---|---|
| Tensile Strength | 68.31 MPa | GB/T 1040.1-2018 |
| Tensile Elongation at Break | 233 % | GB/T 1040.1-2018 |
| Flexural Strength | 89.83 MPa | GB/T 9341-2008 |
| Flexural Modulus | 2121.52 MPa | GB/T 9341-2008 |
| Notched Impact Strength | 8.91 kJ/m² | GB/T 1843-2008 |
Thermal & Processing Properties
| Property | Value | Test Standard |
|---|---|---|
| Heat Deflection Temperature (1.82 MPa) | 49.0 °C | GB/T 1634.1/2-2019 |
| Melt Flow Rate (230°C, 2.16 kg) | 34.89 g/10 min | GB/T 3682-2018 |
Why Choose HENGYI HY245
High Melt Flow: Ideal for fast-cycle injection molding and thin-walled applications
Excellent Elongation: Provides high impact resistance for tough applications
Low Extractables & Moisture: Ensures stable processing and minimal defects
Versatile Base Resin: Suitable for compounding with additives and reinforcements
Balanced Performance: Good stiffness, strength, and impact resistance for a wide range of applications