HENGYI PA6 C500
- Low viscosity nylon for high-speed extrusion
- High tensile strength and elongation
- Good impact resistance for durable products
- Moisture-controlled for stable processing
- Ideal for monofilament, bristle, and textile fiber applications
Product Overview
Hengyi PA6 C500 is a low-viscosity Polyamide 6 (PA6) resin, specifically developed for extrusion and textile applications such as monofilaments, bristles, and fibers.
It provides high tensile strength, excellent elongation, and good impact resistance, making it ideal for use in fiber production, brush filaments, and other extrusion-based products. This resin is moisture-controlled for stable processing and is optimized for high-speed extrusion.
Key Properties
High Tensile Strength & Elongation: Excellent balance of strength and flexibility for fiber applications
Low Viscosity: Optimized for high-speed extrusion and fine filament production
Good Impact Resistance: Provides toughness for durable end-use products
Moisture Controlled: Low moisture content ensures stable processing and performance
Extrusion Grade: Suitable for monofilaments, bristles, and textile fiber applications
Typical Applications
Monofilaments for brushes, sewing threads, and fishing lines
Synthetic Bristles for industrial and household brushes
Textile Fibers and Yarns for fabric and textile production
Extruded Profiles and Tubing for various industrial uses
General Extrusion-based Nylon Products
Technical Data (Typical Values)
Physical Properties
| Property | Value | Test Standard |
|---|---|---|
| Viscosity (Relative to 96% H₂SO₄) | 2.47 ± 0.03 | Internal Method |
| Moisture Content | ≤ 500 ppm | Internal Method |
| Melt Index (230°C, 2.16 kg) | 34.24 g/10min | GB/T 3682-2018 |
Mechanical Properties
| Property | Value | Test Standard |
|---|---|---|
| Tensile Strength (20 mm/min) | 73.76 MPa | GB/T 1040.1-2018 |
| Elongation at Break (20 mm/min) | 214 % | GB/T 1040.1-2018 |
| Flexural Strength (5 mm/min) | 108.47 MPa | GB/T 9341-2008 |
| Flexural Modulus (5 mm/min) | 2440 MPa | GB/T 9341-2008 |
| Izod Notched Impact Strength (23°C, 50% RH) | 7.98 kJ/m² | GB/T 1843-2008 |
Thermal Properties
| Property | Value | Test Standard |
|---|---|---|
| Heat Deflection Temperature (1.82 MPa) | 45.1 °C | GB/T 1634.1 |
Why Choose HENGYI C500
High Tensile Strength & Elongation: Offers excellent flexibility for monofilament and fiber applications
Low Viscosity for Fast Extrusion: Ideal for high-speed extrusion processes
Good Impact Resistance: Ensures durability in demanding end-use applications
Moisture Control: Stable processing with low moisture content
Extrusion Grade: Perfect for synthetic bristles, yarns, and other extrusion-based products