LOYOCON® POM GH-25
- 25% glass fiber reinforced POM
- High tensile strength and stiffness for durable components
- Excellent thermal resistance up to 159.8°C
- Good impact resistance for reliable performance
- Ideal for automotive, industrial, and electrical components
Product Overview
LOYOCON® POM GH-25 is a 25% glass fiber reinforced Polyoxymethylene (POM) copolymer designed for high-performance applications demanding superior strength, high stiffness, and excellent thermal resistance.
Manufactured by Kaifeng Longyu Chemical Co., Ltd., this high-performance composite material provides exceptional mechanical properties, dimensional stability, and resilience under high loads, making it ideal for structural components and components used in harsh environments.
Key Properties
Exceptional Strength & Stiffness: 134.5 MPa tensile strength and 7447 MPa flexural modulus for durable, high-performance parts
High Thermal Resistance: Heat Deflection Temperature (159.8°C) for demanding high-temperature applications
Low Shrinkage: 0.9% shrinkage, ensuring excellent dimensional accuracy in molded parts
Good Impact Resistance: 9.23 kJ/m² Charpy notch impact strength for reliable mechanical performance
Glass Fiber Reinforced: 25% glass fiber content for enhanced mechanical properties
Typical Applications
High-Strength Structural Parts: Automotive components, industrial machinery, and structural components
Automotive Under-Hood Components: Parts requiring high thermal resistance and mechanical strength
Industrial Gears & Bearings: High-performance mechanical parts for machinery
Electrical Insulators & Housings: Components requiring electrical insulation properties and strength
Precision Engineering Components: Parts that demand dimensional accuracy and high durability
Technical Data (Typical Values)
Physical Properties
| Property | Value | Test Standard |
|---|---|---|
| Density | 1.56 g/cm³ | ISO 1183 |
| Shrinkage | 0.9 % | ISO 294 |
| Melt Flow Index (190°C, 2.16kg) | 3.58 g/10min | ISO 1133 |
Mechanical Properties
| Property | Value | Test Standard |
|---|---|---|
| Tensile Strength | 134.5 MPa | ISO 527 |
| Tensile Modulus | 8862 MPa | ISO 527 |
| Elongation at Break | 3.48 % | ISO 527 |
| Flexural Strength | 189.1 MPa | ISO 178 |
| Flexural Modulus | 7447 MPa | ISO 178 |
| Charpy Notched Impact Strength | 9.23 kJ/m² | ISO 179 |
| Rockwell Hardness (M Scale) | 80 | ISO 2039-2 |
Thermal Properties
| Property | Value | Test Standard |
|---|---|---|
| Heat Deflection Temperature (1.8 MPa) | 159.8 °C | ISO 75 |
Why Choose LOYOCON® POM GH-25
25% Glass Fiber Reinforced: Delivers exceptional strength, stiffness, and thermal resistance
High Mechanical Performance: 134.5 MPa tensile strength and 7447 MPa flexural modulus for high durability
High Thermal Resistance: 159.8°C HDT ensures reliability in high-temperature applications
Low Shrinkage: Ensures dimensional accuracy in molded components
Good Impact Resistance: Offers 9.23 kJ/m² for high-performance parts