+86-18958951029
KINGFA PA6-G30 N101
- 30% glass fiber reinforced PA6
- High strength and stiffness for demanding applications
- Excellent thermal resistance up to 220°C
- High electrical insulation properties
- Meets UL94 HB flame rating for safety
Product Overview
Kingfa PA6-G30 N101 is a 30% glass fiber reinforced Polyamide 6 (PA6) designed for high-performance applications.
This grade offers outstanding mechanical strength, stiffness, thermal resistance, and electrical insulation properties, making it suitable for demanding applications in automotive, electrical, and industrial sectors. Its low shrinkage and excellent dimensional stability make it ideal for precision molding and high-stress components.
Key Properties
High Strength & Stiffness: Reinforced with 30% glass fiber for superior mechanical performance
Excellent Thermal Resistance: Heat deflection temperatures up to 220°C for high-temperature applications
Outstanding Electrical Insulation: High volume resistivity and dielectric strength for electrical components
Low Shrinkage & Good Dimensional Stability: Ensures precision molding and high accuracy in parts
Flame Retardant: Meets UL94 HB and Glow Wire Performance for safety in electrical applications
Typical Applications
Automotive: Engine components, structural parts, and high-stress mechanical components
Electrical: Connectors, housings, and insulation components
Industrial: Gears, bearings, and precision parts for high-load applications
Consumer Electronics: Structural components and housings for electrical appliances
Technical Data (Typical Values)
Physical Properties
| Property | Value | Test Standard |
|---|---|---|
| Density | 1.36 g/cm³ | ASTM D792 |
| Molding Shrinkage (Flow) | 0.4 % | ASTM D995 |
| Molding Shrinkage (Cross Flow) | 0.9 % | ASTM D995 |
| Water Absorption (23°C, 24 hr) | 0.6 % | ASTM D570 |
| Ash Content (Glass Fiber) | 30 % | — |
| Rockwell Hardness (R Scale) | 120 | ASTM D785 |
Mechanical Properties (23°C)
| Property | Value | Test Standard |
|---|---|---|
| Tensile Strength | 155 MPa | ASTM D638 |
| Tensile Elongation at Break | 4.1 % | ASTM D638 |
| Flexural Strength | 230 MPa | ASTM D790 |
| Flexural Modulus | 7800 MPa | ASTM D790 |
| Notched Izod Impact | 185 J/m | ASTM D256 |
Thermal Properties
| Property | Value | Test Standard |
|---|---|---|
| HDT (0.45 MPa) | 220 °C | ASTM D648 |
| HDT (1.8 MPa) | 213 °C | ASTM D648 |
Electrical Properties
| Property | Value | Test Standard |
|---|---|---|
| Volume Resistivity | 1 × 10¹⁶ Ω·cm | ASTM D257 |
| Dielectric Strength | 11 kV/mm | ASTM D149 |
| Arc Resistance | 5 PLC | ASTM D495 |
| Comparative Tracking Index (CTI) | 0 PLC | IEC 60112 |
Flame & Safety Properties
| Property | Value | Test Standard |
|---|---|---|
| UL94 Flame Rating | HB (1.6 mm & 3.0 mm) | UL94 |
| Glow Wire Flammability Index (GWFI) | 700 °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (GWIT) | 725 °C | IEC 60695-2-13 |
| UL Relative Thermal Index (RTI) | UL 746B | |
| RTI Electrical (1.6 mm & 3.0 mm) | 130 °C | UL 746B |
| RTI Impact (1.6 mm & 3.0 mm) | 100 °C | UL 746B |
| RTI Strength (1.6 mm & 3.0 mm) | 140 °C | UL 746B |
| HWI / HAI (1.6 mm & 3.0 mm) | 0–2 PLC | UL 746A |
Why Choose KINGFA PA6-G30 N101
30% Glass Fiber Reinforced: Provides superior mechanical strength and stiffness
Outstanding Thermal Resistance: Suitable for high-temperature applications up to 220°C
Excellent Electrical Insulation: High resistivity and dielectric strength for electrical applications
Low Shrinkage: Ensures precision and stability during molding
Flame Retardant: Meets UL94 HB and Glow Wire Performance for safety in critical applications