JUHESHUN PA6 J2700
- High elongation PA6
- Excellent toughness and impact resistance
- Ideal for flame-retardant and toughened compounds
- Low moisture and extractables for stable processing
- Versatile resin for automotive, electronics, and industrial applications
Product Overview
Juheshun PA6 J2700 is a general-purpose Polyamide 6 (PA6) base resin designed for material modification and compounding.
With a balanced viscosity, excellent mechanical properties, and high elongation, it serves as an excellent matrix for flame retardant, toughened, and filled compounds. This resin is widely used across industries such as automotive, electronics, consumer goods, and industrial applications, offering enhanced ductility and processability for high-performance parts.
Key Properties
High Elongation & Toughness: Excellent ductility and impact resistance for modified compounds
Good Processability: Suitable for injection molding and compounding processes
Low Moisture & Extractables: Ensures enhanced stability and consistency during processing
Versatile Base Resin: Ideal for blending with flame retardants, tougheners, and fillers
Balanced Viscosity: Provides good flow properties while maintaining mechanical integrity
Typical Applications
Base polymer for flame-retardant and toughened compounds
Automotive interior and functional components
Electrical tool housings and enclosures
Consumer electronics, furniture, and toy parts
Industrial and mechanical injection molded parts
Technical Data (Typical Values)
Material Specific Properties
| Property | Value | Test Standard |
|---|---|---|
| Relative Viscosity (96% H₂SO₄) | 2.69 | Q/JHSJ001-2019 |
| Hot Water Extractables | 0.24 % | Hot Water Extraction |
| Moisture Content | 0.04 % | Karl Fischer Method |
Mechanical Properties
| Property | Value | Test Standard |
|---|---|---|
| Tensile Strength | 74 MPa | GB/T 1040.1-2018 |
| Tensile Elongation at Break | 214.1 % | GB/T 1040.1-2018 |
| Tensile Modulus | 1160 MPa | GB/T 1040.1-2018 |
| Flexural Strength | 95.4 MPa | GB/T 9341-2008 |
| Flexural Modulus | 2084.47 MPa | GB/T 9341-2008 |
| Notched Impact Strength | 8.84 kJ/m² | GB/T 1843-2008 |
| Hardness (Shore D) | 78.40 HD | GB/T 2411-2008 |
Thermal & Processing Properties
| Property | Value | Test Standard |
|---|---|---|
| Heat Deflection Temperature (1.82 MPa) | 53 °C | GB/T 1634.1/2-2019 |
| Melt Flow Rate (230°C, 2.16 kg) | 20.82 g/10 min | GB/T 3682.1-2018 |
Why Choose JUHESHUN PA6 J2700
High Elongation & Toughness: Provides superior impact resistance and flexibility for modified compounds
Excellent Processability: Ideal for injection molding and compounding applications
Low Moisture & Extractables: Ensures stable processing and high-quality results
Versatile Base Resin: Perfect for blending with flame retardants, tougheners, and fillers
Balanced Viscosity: Ensures consistent flow and performance for high-quality parts