ZPC ABS ZA1300
- Flame retardant with UL 94 HB rating
- Exceptional impact resistance with 35 kJ/m²
- High mechanical strength with 40 MPa tensile strength
- Excellent processing properties with 7-10 g/10min melt index
- Ideal for extruded profiles, industrial components, and pipes
Product Overview
ZPC ABS ZA1300 is an extrusion grade, high impact ABS resin manufactured by Zhejiang Petroleum & Chemical Co., Ltd.
This material offers exceptional impact resistance, good mechanical strength, and UL 94 HB flame retardancy, making it suitable for extrusion molding applications where durability and structural integrity are essential.
With a melt index of 7~10 g/10min and density of 1.04 g/cm³, ZA1300 is designed for stable extrusion processing in profiles, sheets, pipes, and industrial components. Its high tensile strength and flexural strength make it ideal for demanding applications requiring high performance and flame safety.
Key Properties
Physical Properties
| Property | Value | Test Standard |
|---|---|---|
| Density | 1.04 g/cm³ | ASTM D792 |
| Melt Index (220°C, 10kg) | 7–10 g/10min | GB/T 3682 |
Mechanical Properties
| Property | Value | Test Standard |
|---|---|---|
| Tensile Strength (50mm/min) | 40 MPa | GB/T 1040 |
| Flexural Strength (2.0mm/min) | 61 MPa | GB/T 9341 |
| Flexural Modulus (2.0mm/min) | 1800 MPa | GB/T 9341 |
| Izod Notched Impact (23°C, 4mm) | 35 kJ/m² | GB/T 1843 |
Thermal Properties
| Property | Value | Test Standard |
|---|---|---|
| Vicat Softening Temperature (50°C/hr, 50N, 4mm) | 97 °C | GB/T 1633 |
Flammability
| Property | Value | Test Standard |
|---|---|---|
| Flame Rating | HB | UL 94 |
Key Benefits
Exceptional Impact Resistance: 35 kJ/m² Izod notch impact for durable extruded profiles.
Optimized for Extrusion: 7-10 g/10min melt index for stable extrusion processing and high-volume production.
Good Mechanical Strength: 40 MPa tensile strength and 61 MPa flexural strength for structural integrity.
Thermal Stability: 97°C Vicat softening temperature for elevated temperature applications.
Standard Flame Retardancy: UL 94 HB rated for fire safety in industrial applications.
Typical Applications
Extruded Profiles and Sections: Ideal for tough and impact-resistant profiles used in construction and industrial applications.
Sheet and Plate Extrusion: Suitable for sheet and plate applications where aesthetic and mechanical durability are needed.
Pipe and Tube Extrusion: Perfect for extruding pipes and tubes used in industrial piping and fluid transport systems.
Industrial Components: Durable components for machinery and industrial equipment requiring mechanical strength and flame resistance.
Structural Extrusions: Structural parts for heavy-duty machinery and construction.
Why Choose ZPC ABS ZA1300
Flame Retardant: UL 94 HB rated for basic flame safety in electrical and industrial components.
High Impact Resistance: 35 kJ/m² Izod impact ensures long-lasting durability in high-stress environments.
Good Mechanical Strength: Provides 40 MPa tensile strength and 61 MPa flexural strength for high-performance applications.
Stable Processing: With a 7-10 g/10min melt index, ZA1300 ensures smooth extrusion and consistent molding.
Thermal Stability: 97°C Vicat softening temperature ensures stability in moderate temperature environments.